Titanium And Titanium Alloy Plates

Origin: Baoji, Shaanxi, China
Brand: FRL metal
Density: 4.51g/cm³
Grade: GR1、GR2、GR5、GR7、GR9、GR11、GR23
Thickness: 0.3mm to 4.0mm
Standard: ASTM B265、AMS 4911、ASTM F136、AMS 4902
Processing technology: cold rolling/hot rolling
Advantages: high strength and corrosion resistance
Certification: ISO9001
Delivery time: 7-15 days
Packaging Details: Plywood case

Send Inquiry

Download

Product Description

Features of Titanium And Titanium Alloy Plates

1. The oxide film on the surface of titanium and titanium alloy plates is equivalent to a good wear-resistant depilatory agent. The use of titanium plates eliminates the need for depilatory agents, making the plates easy to peel off and avoiding the pretreatment process of plate processing. Titanium plates Half as light as copper plate.

2. The service life of titanium and titanium alloy plates is more than three times that of copper plates, and can reach 10-20 years according to the use conditions

3. The electrolytic copper crystal structure prepared by titanium seed plate is dense, the surface is smooth, and the performance is excellent in quality.

4. Since the titanium and titanium alloy plates do not need to be coated with a separating agent, the pollution of the copper electrolyte can be avoided.

5. Increase the production capacity of electrolytic copper, reduce production costs, and have good economic benefits.

Manufacturing process of Titanium And Titanium Alloy Plates

1. Hot forging is a forging process performed above the metal recrystallization temperature.

2. Hot rolling is a rolling process above the recrystallization temperature.

3. Cold rolling process in which the plastic deformation temperature is lower than the recovery temperature.

4. Annealing: A heat treatment process in which the metal is slowly heated to a certain temperature, held for a sufficient time, and then cooled at an appropriate rate (usually slow cooling, sometimes controlled cooling).

5. Pickling: Immerse the product in an aqueous solution such as sulfuric acid to remove oxide films and other films on the metal surface. It is the pretreatment or intermediate treatment of electroplating, enamel, rolling and other processes.

Titanium And Titanium Alloy Plates Description:

Titanium and Titanium Alloy Plates
Grade	Standard	Production method	Supply status	Specification
				Thickness/mm	Width/mm	Length/mm
Gr1,Gr2,Gr3Gr4 Gr5, Gr7,Gr9, Gr11 Gr12,Gr16,Gr17	ASTM B265 ASTM F136 AMS 4911	hot rolling	R	>4.75-60.0	400-3000	1000-4000
			M
		cold rolling	Y	0.30-4.75	400-2000	1000-3000
			M
			ST
		hot rolling	ST	>4.0-10.0	400-3000	1000-4000
		cold rolling	ST	1.0-4.0	400-1000	1000-3000
		cold rolling	ST	0.3-4.75	400-1000	1000-3000
Tips: Negotiated by both sides, the supply exceeds the specifications of the table.

Titanium And Titanium Alloy Plates Picture display

Customized Titanium And Titanium Alloy Plates

Titanium And Titanium Alloy Plates Chemical Composition:

Grade	chemical composition, weight percent (%)
	C	H	O	N	Fe	Al	V	Pd	Ni	Mo	Ti
	(≤)	(≤)	(≤)	(≤)	(≤)	-	-	-	-	-	bal
GR1	0.08	0.015	0.18	0.03	0.2	-	-	-	-	-	bal
GR2	0.08	0.015	0.25	0.03	0.3	-	-	-	-	-	bal
GR4	0.08	0.015	0.25	0.03	0.3	-	-	-	-	-	bal
GR5	0.08	0.015	0.2	0.05	0.4	5.5~6.75	3.5~4.5	-	-	-	bal
GR7	0.08	0.015	0.25	0.03	0.3	-	-	0.12~0.25	0.12~0.25	-	bal
GR9	0.08	0.015	0.15	0.03	0.25	2.5~3.5	2.5~3.5	-	-	-	bal
GR11	0.08	0.15	0.18	0.03	0.2	-	-	0.12~0.25	-	-	bal
GR12	0.08	0.15	0.25	0.03	0.3	-	-	-	0.6~0.9	0.2~0.4	bal
GR23	0.08	0.125	0.13	0.03	0.25	5.5~6.5	3.5~4.5	-	-	-	bal

Titanium And Titanium Alloy Plates Surface Description:

Surface	Definition	Application
No.1	The surface is finished by heat treatment and pickling or processes corresponding there to after hot rolling.	Chemical tank, pipe, etc.
No.3	Those finished by polishing with No.100 to No.120 abrasives specified in JIS R6001.	Kitchen utensils, Building construction, etc.
No.4	Those finished by polishing with No.150 to No.180 abrasives specified in JIS R6001.	Kitchen utensils, Building construction, Medical equipment, etc.
2B	Those are finished, after cold rolling, by heat treatment, pickling, or other equivalent treatment, and lastly by cold rolling to give appropriate luster.	Medical equipment, Food industry, Construction material, Kitchen utensils, etc.
BA (No.6)	Those processed with bright heat treatment after cold rolling.	Kitchen utensils, Electric equipment, Building construction, etc.
Mirror (No.8)	Shinning like a mirror	Building construction, decoration, etc.
Hairline	Those finished polishing so as to give continuous polishing streaks by using abrasive of suitable grain size.	Building Construction etc.

Our Packaging

Package

About us

Baoji Freelong New Material Technology Development Co., Ltd loated in Baoji City--China's Titanium Valley,we are mainly doing Zirconium,Titanium,Nickel,Niobium,Tantalum etc metal material and other alloy's produce,OEM and Sales.and also exporting the goods what we make. we have a lot of trustful clients and partner.and also we were authority by some firms.At present,we were build our relationship with Australia,Korea,German,US,UK,Malaysia,AZ,Middle East,Taiwan,Etc. Our company always take the quality and service as our responsibility,We always get close even match the quality what our customer wanted and as for quality,we never say no and no reason for quality failure.

Our Factory